A method for preparing powder for wireless charging according to an embodiment comprises: a temperature-raising step of raising the temperature of iron-containing raw material particles up to a low-temperature heat treatment temperature of 600 °C or less in an oxygen-containing atmosphere for 30 minutes to 2 hours; and a heat treatment step of maintaining the temperature at the low-temperature heat treatment temperature for 1-10 hours to prepare powder for wireless charging in which an insulating layer is formed on the surfaces of the iron-containing raw material particles, thereby preparing powder for wireless charging having a current loss reduction index of 1.1 to 3 according to equation 1 defined in the detailed description of the present invention. By reducing loss, the powder can be used for wireless charging of electric vehicles, drones, and the like.

    Un procédé de préparation de poudre pour charge sans fil selon un mode de réalisation comprend: une étape d'élévation de la température consistant à élever la température de particules de matière première contenant du fer à une température de traitement thermique basse température de 600 °C ou moins dans une atmosphère contenant de l'oxygène pendant 30 minutes à 2 heures; et une étape de traitement thermique consistant à maintenir la température à la température de traitement thermique basse température pendant 1 à 10 heures pour préparer une poudre pour charge sans fil, dans laquelle une couche isolante est formée sur les surfaces des particules de matière première contenant du fer, ce qui permet de préparer une poudre pour charge sans fil ayant un indice de réduction de perte de courant de 1,1 à 3 selon l'équation 1 définie dans le descritpif de la présente invention. En réduisant la perte, la poudre peut être utilisée pour la charge sans fil de véhicules électriques, de drones et autres.

    실시예의 무선충전용 파우더의 제조방법 등은 산소 함유 분위기에서 철 함유 원료입자를 600 ℃ 이하의 저온열처리온도까지 30분 내지 2시간 동안 승온하는 승온단계; 그리고 상기 저온열처리온도에서 1 내지 10시간 동안 유지하여 상기 철 함유 원료입자의 표면에 절연층이 형성된 무선충전용 파우더를 마련하는 열처리단계;를 포함하여, 발명의 상세한 설명에서 정의한 식 1에 따른 전류손실저감지수가 1.1 내지 3의 값을 갖는 무선충전용 파우더를 제조하며, 손실을 줄여 전기자동차, 드론 등의 무선충전용으로 활용될 수 있다.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    POWDER FOR WIRELESS CHARGING, PREPARATION METHOD THEREFOR, AND PAD FOR WIRELESS CHARGING COMPRISING SAME


    Weitere Titelangaben:

    POUDRE POUR CHARGE SANS FIL, SON PROCÉDÉ DE PRÉPARATION, ET BASE POUR CHARGE SANS FIL COMPRENANT CELLE-CI
    무선충전용 파우더, 이의 제조방법 및 이를 포함하는 무선충전용 패드


    Beteiligte:
    PARK JONGHWI (Autor:in) / CHOI JONGHAK (Autor:in) / LEE SEUNGHWAN (Autor:in) / KIM NAYOUNG (Autor:in) / KIM TAEKYOUNG (Autor:in)

    Erscheinungsdatum :

    2020-09-24


    Medientyp :

    Patent


    Format :

    Elektronische Ressource


    Sprache :

    Koreanisch


    Klassifikation :

    IPC:    B22F Verarbeiten von Metallpulver , WORKING METALLIC POWDER / B60L PROPULSION OF ELECTRICALLY-PROPELLED VEHICLES , Antrieb von elektrisch angetriebenen Fahrzeugen / H01F MAGNETS , Magnete / H02J CIRCUIT ARRANGEMENTS OR SYSTEMS FOR SUPPLYING OR DISTRIBUTING ELECTRIC POWER , Schaltungsanordnungen oder Systeme für die Abgabe oder Verteilung elektrischer Leistung




    WIRELESS CHARGING PAD WIRELESS CHARGING DEVICE AND ELECTRIC VEHICLE COMPRISING SAME

    KIM TAE KYOUNG / KIM NAH YOUNG / CHOI JONGHAK et al. | Europäisches Patentamt | 2021

    Freier Zugriff

    WIRELESS CHARGING PAD WIRELESS CHARGING DEVICE AND ELECTRIC VEHICLE COMPRISING SAME

    KIM TAE KYOUNG / KIM NAH YOUNG / CHOI JONGHAK et al. | Europäisches Patentamt | 2021

    Freier Zugriff

    WIRELESS CHARGING PAD WIRELESS CHARGING DEVICE AND ELECTRIC VEHICLE COMPRISING SAME

    KIM NAH YOUNG / CHOI JONGHAK / KIM TAE KYOUNG et al. | Europäisches Patentamt | 2021

    Freier Zugriff