PROBLEM TO BE SOLVED: To provide a rubber/cord composite material with sufficiently secured adhesiveness between a steel cord and a topping rubber, even when vulcanized at a relatively low temperature of about 150.SOLUTION: A rubber/cord composite material 9 comprises a steel cord 10 comprising plated element wires 13 and a topping rubber 12 for covering the steel cord 10. The plated element wire 13 comprises a core wire 13A and a ternary plated layer 13B of copper (Cu), zinc (Zn) and cobalt (Co), formed on the surface of the core wire 13A. The ternary plated layer 13B contains 55 to 78 parts by mass of copper (Cu) and 0.5 to 8.0 parts by mass of cobalt (Co) relative to 100 parts by mass of the plating. The topping rubber 12 contains 5 parts by mass or more of silica relative to 100 parts by mass of the rubber component.SELECTED DRAWING: Figure 2
【課題】150程度の比較的低い温度で加硫してもスチールコードとトッピングゴムとの接着性を充分に確保するゴム・コード複合体の提供。【解決手段】メッキ素線13からなるスチールコード10と、スチールコード10を被覆するトッピングゴム12とからなるゴム・コード複合体9で、メッキ素線13は、芯線13Aと、芯線13Aの表面に形成されかつ銅(Cu)、亜鉛(Zn)、及び、コバルト(Co)からなる3元メッキ層13Bとを含んでおり、3元メッキ層13Bは、メッキ100質量部に対して、銅(Cu):55〜78質量部、及び、コバルト(Co):0.5〜8.0質量部を含み、トッピングゴム12は、ゴム成分100質量部に対してシリカを5質量部以上含んでいるゴム・コード複合体。【選択図】図2
RUBBER/CORD COMPOSITE MATERIAL, AND PNEUMATIC TIRE MADE THEREFROM
ゴム・コード複合体、及びそれを用いた空気入りタイヤ
2017-06-08
Patent
Elektronische Ressource
Japanisch
STEEL CORD FOR REINFORCING RUBBER PRODUCT, AND PNEUMATIC TIRE MADE THEREFROM
Europäisches Patentamt | 2017
|