The invention relates to acid-resistant steel as well as a preparation method and application thereof. The acid-resistant steel comprises the following chemical components: C, Si, Mn, P, S, Al, Nb, V, Cr, Sb, Ni, N and Fe. Wherein the content of the C is 0.010%-0.025% by mass, the content of the Mn is 0.2%-0.4% by mass, the content of the Cr is 1.3%-2.0% by mass, the content of the Sb is 0.03%-0.07% by mass, and the content of the Ni is 0.05%-0.10% by mass; and the following relational expression is satisfied: [Ni]/[Sb] > = 1.0. According to the acid-resistant steel, the yield strength reaches 1000 MPa or above, the tensile strength reaches 1100 MPa or above, the ductility reaches 5% or above, meanwhile, compared with Q345, the sulfuric acid corrosion resistance is improved by 50% or above, and cracking is avoided when 90-degree d = 1a small-angle bending is achieved.

    本申请涉及一种耐酸钢及其制备方法与应用,所述耐酸钢的化学成分包括:C、Si、Mn、P、S、Al、Nb、V、Cr、Sb、Ni、N以及Fe;其中,以质量分数计,C的含量为0.010%~0.025%,Mn的含量为0.2%~0.4%,Cr的含量为1.3%~2.0%,Sb的含量为0.03%~0.07%,Ni的含量为0.05%~0.10%;且满足如下关系式:[Ni]/[Sb]≥1.0。该耐酸钢的屈服强度达到1000MPa以上,抗拉强度达到1100MPa以上,延伸率达到5%以上,同时较Q345耐硫酸腐蚀性能提升50%以上,并满足90°d=1a小角度折弯不开裂。


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Acid-resistant steel as well as preparation method and application thereof


    Weitere Titelangaben:

    一种耐酸钢及其制备方法与应用


    Beteiligte:
    HUI YAJUN (Autor:in) / CAI AYUN (Autor:in) / LIU KUN (Autor:in) / HAN YUN (Autor:in) / TIAN ZHIHONG (Autor:in) / WANG MINGZHE (Autor:in) / LIU LIWEI (Autor:in) / WANG CHANG (Autor:in)

    Erscheinungsdatum :

    09.04.2024


    Medientyp :

    Patent


    Format :

    Elektronische Ressource


    Sprache :

    Chinesisch


    Klassifikation :

    IPC:    C22C Legierungen , ALLOYS / C21D Veränderung der physikalischen Struktur von Eisenmetallen , MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS / B21B Walzen von Metall , ROLLING OF METAL / B62D MOTOR VEHICLES , Motorfahrzeuge



    Austenite light wear-resistant steel as well as preparation method and application thereof

    WANG QINGFENG / LIU RIPING / ZHANG XINYU et al. | Europäisches Patentamt | 2024

    Freier Zugriff

    Heat-resistant tread rubber as well as preparation method and application thereof

    YU HUAYING / LIN QIANJIN / ZHANG XIANHUI et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Wear-resistant insulating paint as well as preparation method and application thereof

    ZENG FANHUI / LI JIANLIN / WANG MINGXING | Europäisches Patentamt | 2023

    Freier Zugriff

    Waterproof wear-resistant coating as well as preparation method and application thereof

    TAN GUOHUANG / WU XINGHUA / PAN YUTONG et al. | Europäisches Patentamt | 2023

    Freier Zugriff

    Low-density corrosion-resistant steel and preparation method and application thereof

    LIU RIPING / WANG FEI / WANG SUOTAO et al. | Europäisches Patentamt | 2020

    Freier Zugriff