The invention discloses a wet-skid-resistant tire tread rubber material with high road holding force and a tire. The tire tread rubber material comprises the following raw materials in parts by mass: 50-60 parts of Yunnan 10 # rubber; 45 to 50 parts of SBR1723 (styrene butadiene rubber 1723); 8 to 12 parts of BR9000 and 75 to 80 parts of environment-friendly reclaimed rubber; 35 to 38 parts of N220; 35 to 38 parts of thermal cracking carbon black and 18 to 22 parts of white carbon black; 2.5 to 3 parts of SI69; 4 to 6 parts of ZnO; 2.5 to 3.5 parts of SA; 3 to 5 parts of 6PP (4020); 2.5 to 3 parts of an anti-aging agent RD; 5-6 parts of phenolic resin; 3 to 3.5 parts of microcrystalline wax; 14 to 15 parts of naphthenic oil; 2 to 2.5 parts of vulcanizing agent S; 1 to 1.5 parts of a vulcanizing agent CBS; 0.1 to 0.2 part of a vulcanizing agent CTP.
本申请公开了一种抗湿滑高抓地力轮胎胎面胶料和轮胎,所述轮胎的胶料的各原料及各原料的质量份配比如下:云南10#胶为50‑60份;SBR1723为45‑50份;BR9000为8‑12份,环保再生胶为75‑80份;N220为35‑38份;热裂解炭黑为35‑38份,白炭黑为18‑22份;SI69为2.5‑3份;ZnO为4‑6份;SA为2.5‑3.5份;6PPD(4020)为3‑5份;防老剂RD为2.5‑3份;酚醛树脂为5‑6份;微晶蜡为3‑3.5份;环烷油为14‑15份;硫化剂S为2‑2.5份;硫化剂CBS为1‑1.5份;硫化剂CTP为0.1‑0.2份。
Wet-skid-resistant high-road-holding-force tire tread rubber material and tire
一种抗湿滑高抓地力轮胎胎面胶料和轮胎
2023-10-20
Patent
Elektronische Ressource
Chinesisch
IPC: | C08L COMPOSITIONS OF MACROMOLECULAR COMPOUNDS , Massen auf Basis makromolekularer Verbindungen / B60C VEHICLE TYRES , Fahrzeugreifen / C08K Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe , USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS |
Europäisches Patentamt | 2024
|High-wet-wet-holding wet-skid-resistant tread rubber composition, mixing method and car tire
Europäisches Patentamt | 2023
|Ultra-high road holding tire tread rubber composition, preparation method thereof and car tire
Europäisches Patentamt | 2023
|High-road-holding-force tire tread and preparation method thereof
Europäisches Patentamt | 2024
|