The invention provides a high-performance truck tire tread rubber material. The high-performance truck tire tread rubber material is prepared from the following raw material components: 25-35 parts of natural rubber; 30-40 parts of butadiene rubber; 15-25 parts of styrene butadiene rubber; 1-3 parts of sulfur; 1-4 parts of an accelerant; 5-10 parts of modified resin; 40-60 parts of high wear resistance carbon black; 10 to 20 parts of white carbon black; 3-5 parts of zinc oxide; 3-5 parts of stearic acid; 1-4 parts of a silane coupling agent; and 1-3 parts of an anti-aging agent. Compared with a conventional truck tire formula and unmodified resin, the rubber material prepared from the modified resin has the beneficial effects that the wear resistance is enhanced, the rolling resistance is reduced, and the wet skid resistance is also improved.
本发明提供了一种高性能载重胎胎面胶料,其制备原料包括以下组分:天然橡胶25‑35份;顺丁橡胶30‑40份;丁苯橡胶15‑25份;硫磺1‑3份;促进剂1‑4份;改性树脂5‑10份;高耐磨炭黑40‑60份;白炭黑10‑20份;氧化锌3‑5份;硬脂酸3‑5份;硅烷偶联剂1‑4份;防老剂1‑3份。本发明的有益效果为:与常规载重胎配方和未改性树脂相比,使用改性树脂制备的胶料耐磨性增强,滚动阻力降低,且抗湿滑性也有所改善。
High-performance truck tire tread rubber material
一种高性能载重胎胎面胶料
2022-11-08
Patent
Elektronische Ressource
Chinesisch
IPC: | C08L COMPOSITIONS OF MACROMOLECULAR COMPOUNDS , Massen auf Basis makromolekularer Verbindungen / B60C VEHICLE TYRES , Fahrzeugreifen / C08K Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe , USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS |