本发明的课题是提供一种疲劳性、低放热性以及拉伸特性均优异的硫化橡胶的原料、亦即橡胶湿法母炼胶的制造方法。可以利用以下方法来制造橡胶湿法母炼胶,该方法包括:准备镁含量为150ppm以下的胶乳的工序和制作包含橡胶成分及炭黑的混合液的工序。胶乳可以包含90体积%粒径为2μm以下的橡胶粒子。制作混合液的工序可以包括将胶乳和分散溶剂混合的步骤(a)和将包含炭黑的浆料及利用步骤(a)得到的胶乳溶液混合的步骤(b)。橡胶湿法母炼胶的制造方法可以满足下式I。0.1<b/a<1.0(式I)(式I中,a表示胶乳的镁含量(ppm)。b表示混合液中的炭黑相对于混合液的橡胶成分100质量份的量(质量份)。

    A method of manufacturing a wet rubber masterbatch includes preparing latex containing magnesium in an amount which is not greater than 150 ppm; and making a liquid mixture that includes a rubber component and carbon black. The latex may include rubber particles for which the 90 vol % particle diameter is not greater than 2 μm. The liquid mixture can be made by a step (a) in which the latex and a dispersion solvent are mixed; and a step (b) in which a latex solution obtained at step (a) and a slurry containing the carbon black are mixed. The method for manufacturing a wet rubber masterbatch may satisfy: 0.1<1.0, where a indicates amount (ppm) of magnesium present in latex; and b indicates amount (parts by mass) of carbon black in the liquid mixture for every 100 parts by mass of rubber component in the liquid mixture.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    橡胶湿法母炼胶的制造方法、橡胶组合物的制造方法以及轮胎的制造方法


    Erscheinungsdatum :

    2020-12-29


    Medientyp :

    Patent


    Format :

    Elektronische Ressource


    Sprache :

    Chinesisch


    Klassifikation :

    IPC:    C08J Verarbeitung , WORKING-UP / B60C VEHICLE TYRES , Fahrzeugreifen / C08C TREATMENT OR CHEMICAL MODIFICATION OF RUBBERS , Behandlung oder chemische Modifizierung von Kautschuken / C08K Verwendung von anorganischen oder nichtmakromolekularen organischen Stoffen als Zusatzstoffe , USE OF INORGANIC OR NON-MACROMOLECULAR ORGANIC SUBSTANCES AS COMPOUNDING INGREDIENTS / C08L COMPOSITIONS OF MACROMOLECULAR COMPOUNDS , Massen auf Basis makromolekularer Verbindungen