The purpose of this study is AlZn-based produced by high speed mechanical alloying method to investigate the effect of Zn amount on the composite material, Al-Zn-Mg-Cu-SiC composite material billets are obtained by sintering.
Mechanical alloying, X-ray diffraction analysis (XRD) graphics, sintering, polishing, scanning electron microscopy and energy dispersive X-ray analyzer (EDX) images and micro hardness tests were applied, respectively.
In the XRD analysis results, it was observed that the Al peak height decreased as the alloying time increased. When the samples sintered for 90 min are examined, it can be clearly seen that the hardness increases as the Zn ratio increases. EDX analysis results also support XRD results.
Increase in strength will require the use of thinner sheet metal and smaller rivets to achieve the same strength. This will reduce the weight of the aircraft. Weight reduction also means less fuel consumption and more economical flight. This increase in strength is a very important scientific achievement.
Effect of Zn amount on AlZn-based composite material produced by high speed mechanical alloying method
Aircraft Engineering and Aerospace Technology ; 96 , 10 ; 1295-1301
21.11.2024
7 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
AlZn coating of water and gas line tubes
Tema Archiv | 1992
|Hydrogen storage material based on LaNi5 alloy produced by mechanical alloying
Online Contents | 2001
|Intermetallic systems produced by mechanical alloying
Tema Archiv | 1988
|Emerald Group Publishing | 2023
|