Abstract Deorbit sails are used in low earth orbit to reduce the growing amount of orbital debris by rapidly removing satellites at the end of their operational missions. However, in low earth orbit, atomic oxygen (AO) is a potential threat to long-duration exposure facilities. In this work, a multi-faceted simulation for the AO erosion of the Taurus Deorbit Sail was developed to calculate the erosion yield for the membrane material and the undercutting profile at the crease site. The disintegration and erosion detail for the deorbit sail membrane during AO impacts can be studied on an atomic scale. The ReaxFF reaction force field program is used to provide a large enough calculation speed in the size of the system to describe all the chemical reactions of the reaction. The on-orbit flight data from the Materials International Space Station Experiment 2 were used to validate the simulated erosion rate in this study. The defects on the deorbit sails were experimentally measured using a scanning electron microscope and then modeled by the Monte Carlo method. The computational predictions of AO undercutting at the defect sites were validated by experimental data from the NASA long-duration exposure facility. The disintegration of the membrane could be divided into two stages: the physical reaction stage and the chemical reaction stage, after 150 AO collisions the membrane becomes highly volatilized. The maximum undercutting depth for the deorbit drag sail within the predicted 37-month deorbit time was 5.5 μm and 7.5 μm for a defect width of 500 nm and 1 μm, respectively. The undercutting width for a deorbit sail with a width of 500 nm or 1 μm was predicted to be 1.6 μm and 2 μm, respectively, and the breaker was formed at the bottom of the undercutting profile. AO erosion has been studied by researchers in terms of evaluating the effectiveness of protective coatings. This current study, however, seeks to understand the fundamental interactions between AO and creases in the deorbit sail, which provides deeper knowledge than what has been developed so far. The multi-faceted simulation results can provide design references for engineering applications for the deorbit sail.

    Highlights Erosion of a deorbit sail membrane due to impacts of atomic oxygen was simulated. The disintegration and erosion mechanism is simulated by Molecular dynamics using ReaxFF force field. Deorbit time and atomic oxygen fluence were estimated under actual space conditions. Undercutting profiles were modeled via Monte Carlo and validated using NASA experimental data. Simulation results can provide design reference for the engineering of deorbit sails.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Multi-faceted simulation of atomic oxygen erosion of deorbit sail for cleaning space debris


    Beteiligte:
    Fu, Yulei (Autor:in) / Peng, Fujun (Autor:in) / Zhang, Chongfeng (Autor:in) / Sun, Chengyue (Autor:in) / Zeng, Zhankui (Autor:in) / Fang, Guangqiang (Autor:in)

    Erschienen in:

    Acta Astronautica ; 187 ; 61-69


    Erscheinungsdatum :

    2021-06-10


    Format / Umfang :

    9 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    SPACE DEBRIS ENGAGEMENT AND DEORBIT SYSTEM

    BARNES NATHANIEL C | Europäisches Patentamt | 2020

    Freier Zugriff

    SPACE DEBRIS ENGAGEMENT AND DEORBIT SYSTEM

    BARNES NATHANIEL C | Europäisches Patentamt | 2021

    Freier Zugriff

    SPACE DEBRIS ENGAGEMENT AND DEORBIT SYSTEM

    BARNES NATHANIEL C | Europäisches Patentamt | 2022

    Freier Zugriff

    Space debris engagement and deorbit system

    BARNES NATHANIEL C | Europäisches Patentamt | 2021

    Freier Zugriff