Abstract Ir–Zr co-deposition coatings with 71at% Zr were deposited on graphite by double glow plasma at 1073–1123K. The structure and composition of the coatings were confirmed by FE-SEM, XRD, XPS and EDS. The hardness and the elastic modulus of the coatings were estimated by nanoindentation instrument. The adhesion strength between the coating and the substrate was evaluated by a scratch tester. The results showed that the coating was composed of nanocrystalline grains with a size of 80–90nm compared with 0.5μm for the pure Ir coating. The fine grains of the coatings might be attributed to the additional Zr element. New phases IrZr and ZrC were formed due to the high content of Zr and high deposition temperature. The hardness and elastic modulus of the coatings were about 7.5GPa and 388GPa, respectively. The adhesive force between the coating and the substrate was about 10N.

    Highlights ► A novel design for the co-deposition of Ir-containing Zr coating was fabricated. ► A new phase IrZr compound was formed due to the high substrate temperature. ► The grain size of the Ir–Zr coating decreased with the additional Zr element.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Co-deposition of Ir-containing Zr coating by double glow plasma


    Beteiligte:
    Cong, Xiangna (Autor:in) / Chen, Zhaofeng (Autor:in) / Wu, Wangping (Autor:in) / Chen, Zhou (Autor:in) / Edmond Boafo, Fred (Autor:in)

    Erschienen in:

    Acta Astronautica ; 79 ; 88-95


    Erscheinungsdatum :

    2012-02-23


    Format / Umfang :

    8 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Study on double-glow plasma niobium surface alloying of pure titanium

    Wang, Wenbo / Xu, Zhong / He, Zhiyong et al. | Tema Archiv | 2007


    Coating, Plasma Spray Deposition

    SAE Technical Papers | 2012


    COATING, PLASMA SPRAY DEPOSITION

    SAE Technical Papers | 1994


    COATING, PLASMA SPRAY DEPOSITION

    SAE Technical Papers | 1981