Various measures for prevention of rail end fracture caused by corrosion fatigue cracking were examined by field tests; in preliminary test, 25 measures for prevention of corrosion were examined in tunnels under steam traction; considering test results, 4 measures were selected for life test; life test results showed that in tunnel, in which mean life of nontreated rail was only 3 yr, that of shot-peened rail covered with zinc metalicon was elongated up to 5 or 6 yr.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    Field test of corrosion prevented rails on their endurance limit to rail end fracture


    Weitere Titelangaben:

    Tokyo. Ry Tech Research Inst -- Quarterly Report


    Beteiligte:
    Hirose, S. (Autor:in) / Kose, Y. (Autor:in) / Sato, Y. (Autor:in) / Takihara, M. (Autor:in) / Tomita, K. (Autor:in) / Takeuchi, Y. (Autor:in) / Tsuyuki, S. (Autor:in)


    Erscheinungsdatum :

    1968


    Format / Umfang :

    4 pages


    Medientyp :

    Report


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    Endurance properties of rails

    Mast, P. | Engineering Index Backfile | 1930


    Endurance of steel rails

    Engineering Index Backfile | 1886


    Strength and endurance of steel rails

    Howard, James E. | Engineering Index Backfile | 1908


    Protection of rails against wear and corrosion, rail fractures

    De Benedetti, C. | Engineering Index Backfile | 1932


    Rails and rail failures

    Gennet, Jr., C.W. | Engineering Index Backfile | 1929