Various processes of thermally treating rails, developed in United States, Canada and Europe to prevent formation of shatter cracks, now generally accepted as nuclei from which transverse fissures grow; controlled cooling; author points out that etch and service tests show that process of thermal treatment definitely prevents formation of shatter cracks. Before Univ Mich-Life Conference on New Technologies in Transportation. (see also Ry Gaz v 73 n 2 July 12 1940 p 39-40)


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen


    Exportieren, teilen und zitieren



    Titel :

    No shatter cracks in rail -- No transverse fissures


    Weitere Titelangaben:

    Ry Age


    Beteiligte:
    Woschitz, J.F. (Autor:in)

    Erschienen in:

    Railway Age ; 108 , n 15


    Erscheinungsdatum :

    1940


    Format / Umfang :

    3 pages


    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch


    Schlagwörter :


    No shatter cracks in rail -- No transverse fissures

    Woschitz, J.F. | Engineering Index Backfile | 1940


    Interior transverse rail fissures

    Dudley, P.H. | Engineering Index Backfile | 1916


    Transverse fissures cause rail failures

    Engineering Index Backfile | 1918


    Internal transverse cracks and fissures in rails

    Job, Robert | Engineering Index Backfile | 1914


    Internal transverse cracks and fissures, in rails

    Job, Robert | Engineering Index Backfile | 1915