Selective laser melting (SLM) was used to fabricate Hastelloy X alloy. The characteristics of grains and precipitates in Hastelloy X alloy processed by heat treatments (HT) and hot isostatic pressing (HIP) was analyzed. Furthermore, the tensile property of Hastelloy X alloys at ambient temperature and elevated temperature was investigated. Some grains exhibit columnar crystal morphology in vertically built samples, while the grains are equiaxial in horizontally built samples. The carbide phases with cubic structure are formed within grains and at grain boundaries simultaneously after a combination of HT and HIP. The horizontally built samples exhibits high tensile strength and low plasticity compared with the vertically built ones. Both of vertically built and horizontally built samples show predominantly ductile failure as characterized by dimpled microstructure. The tensile strength of Hastelloy X alloy at ambient temperature produced by SLM is 95% higher than that of hot forged alloy, while the tensile strength at 600℃ is about 85% of hot forged ones.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Anisotropy of Microstructure and Mechanical Properties of Hastelloy X Alloy Produced by Selective Laser Melting


    Beteiligte:
    ZHANG Yongzhi (Autor:in) / HOU Huipeng (Autor:in) / PENG Shuang (Autor:in) / WANG Jie (Autor:in) / WANG Yin (Autor:in) / LEI Liming (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Microstructure and Properties of AlSi10Mg Powder for Selective Laser Melting

    TANG Pengjun / HE Xiaolei / YANG Bin et al. | DOAJ | 2018

    Freier Zugriff

    Laser Surface Melting Treatment on Magnesium Alloy AZ91D: Relationship Between Laser Parameters-Microstructure and Mechanical Properties

    Taltavull, C. / Torres, B. / Lopez, A.J. et al. | British Library Conference Proceedings | 2014


    Thermomechanical treatment of TiAl6V4 alloy fabricated by selective laser melting: optimization of microstructure and fatigue properties

    Kasperovich, Galina / Hausmann, Joachim | Deutsches Zentrum für Luft- und Raumfahrt (DLR) | 2013

    Freier Zugriff


    Microstructure and Mechanical Properties of Laser Melting Deposited TA15+Ti2AlNb Alloys

    LIU Yantao / ZHANG Yongzhong / CHEN Yiqiang et al. | DOAJ | 2017

    Freier Zugriff