Partial block-dropping phenomenon was existed during the precision process of TA15 titanium alloy casting. In view of multiple means of microscopic physical characterization analysis such as OM/SEM/EDS/XRD and by considering the tensile performance results, the microstructure and mechanical properties between block-dropping area and the regular areahad been investigated. This article focused on the impact mechanism on tensile behavior that generated from the abnormal structure of block-dropping area. The results reveal that both the block-dropping area and the regular area show bi-modal microstructure, whereas the β phase concentration of the block-dropping area is far beyond the regular area and emerges as β spot. Microanalysis shows that the segregation of Fe is the major factor causing the abnormal structure and β spot, as well as the sharp plasticity decreases of alloy. The segregated Fe alters the microstructure and properties of the alloy, mainly because the saturation of Fe in α-Ti is only 0.1%, which leads to the formation of brittle TiFe eutectic phase. The increase of strength reduces the plasticity of the alloy casting, and further lead to the block-dropping during the process.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Formation of abnormal structure in ZTA15 titanium alloy casting and its impact mechanism on tensile behavior


    Beteiligte:
    LIU Gaoyang (Autor:in) / ZHAO Wenxia (Autor:in) / WANG Xi (Autor:in)


    Erscheinungsdatum :

    2020




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt