In order to develop a self-lubricating coating with long life and high reliability suitable for harsh working conditions, the composite coating with NiCoCrAlYTa as matrix phase, Ag as lubricant phase and Mo as the reinforcing phase were prepared by high-velocity oxy-fuel spraying(HVOF)technology. The high-low temperature cycling tribological properties of the composite coating were investigated at 25 ℃ and 800 ℃. The morphology features, chemical composition and phase structure of the worn surface were studied to reveal the interaction between different elements in the friction process and physicochemical nature of friction interface. In addition, the multi-cycles adaptive lubrication mechanism under the alternating environment of high and low temperature was explored as well. The results show that the composite coating is dense and uniform, and has better mechanical properties. The phases of the composite coating mainly contain γ-Ni, β-NiAl, γ'-Ni3Al, Ag and Mo. The β-Ag2MoO4 layer-like lubricant generated on the surface can greatly improve the friction and wear performance of the composite coating at high temperature. Under the condition of multi-cycles, the friction coefficient of subsequent cycle of the composite coating is increased compared with the first cycle, but the wear rate of the composite coating at room temperature is decreased. This is caused by the interaction between the lubricating phase of β-Ag2MoO4 and the hard phases of Al2O3 and MoO3 with the action of frictional shear force.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Preparation of NiCoCrAlYTa/Ag/Mo composite self-lubricant coating and its high-low temperature cycling tribological properties


    Beteiligte:
    HAO Enkang (Autor:in) / CHEN Jie (Autor:in) / LIU Guang (Autor:in) / CUI Lang (Autor:in) / WANG Xiaoxia (Autor:in) / WEI Liankun (Autor:in) / AN Yulong (Autor:in)


    Erscheinungsdatum :

    2023




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Vacuum tribological behaviour of self lubricant quasicrystalline composite coatings

    Garcia de Blas, F.J. / Roman, A. / De Miguel, C. et al. | Tema Archiv | 2003


    Vacuum Tribological Behaviour of Self Lubricant Quasicrystalline Composite Coatings

    de Blas, F. J. G. / Roman, A. / De Miguel, C. et al. | British Library Conference Proceedings | 2003


    Tribological Properties of the Lubricant Released by Temperature-Sensitive Hydrogel

    Li, Yue / Guo, Junde / Dong, Guozhong et al. | British Library Online Contents | 2017


    Research on the Tribological Properties of Layered Kaolin Lubricant Additives

    Chang, Jian / Zhang, Li / Song, Shaoze et al. | SAE Technical Papers | 2023