Aiming at a new Al-Li alloy,by the use of optical microscope, SEM and EDS, we analyzed the effects of different pretreatment processes including alkali corrosion and tri-acid deoxidation on the appearance, corrosion resistance and fatigue properties of sulfuric acid anodic oxide coatings. which provided a theoretical basis for the design, selection, application and surface protection of Al-Li alloy structural components. We found that the corrosion degree of the Al-Li alloy surface by alkali corrosion was deeper than that of the tri-acid deoxidation process. The corrosion resistance at the grain boundary was poor, so the mesh surface morphology of the anodic oxide film was formed. The fatigue life of the samples treated with alkali corrosion was lower than that of the tr-ioxic acid treatment, the fatigue life of the samples subjected to sulfuric acid anodic oxidation is different. The effect of different pretreatment on the corrosion resistance of the sulfuric acid anodic oxide layer of Al-Li alloy is not significant.
Effect of Pretreatment Process on Properties of Aerospace Al-Li Alloy Sulfuric Acid Anodic Film
2017
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Anodic Treatment of Aluminum Alloys Sulfuric Acid Process Thin Film
SAE Technical Papers | 2022
ANODIC TREATMENT FOR ALUMINUM BASE ALLOYS Sulfuric Acid Process
SAE Technical Papers | 1958
ANODIC TREATMENT OF ALUMINUM BASE ALLOYS Sulfuric Acid Process
SAE Technical Papers | 1962
Anodic Coating on Aluminum Alloys Sulfuric Acid Process, Resin-Sealed
SAE Technical Papers | 2013
Anodic Treatment of Aluminum Alloys Sulfuric Acid Process, Undyed Coating
SAE Technical Papers | 2003