In order to compare and analyse the effect of two different kinds of forming process on composite mode I interlaminar fracture toughness, the DCB specimens were tested by using hypothesis inspeetion method.A finite element model was also used to simulate the crack propagation process.The results demonstrate that the average of mode I interlaminar fracture toughness from silicon rubber flexible mold forming is a bit higher than that from metal rigid mold forming.Howevers the variance of mode I interlaminar fracture toughness from the two groups shows no significant difference.The crack propagation process of the two forming process is similar. The established finite element model, which is identical to the test results, can predict the process of the crack expansion effectively.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effects of Forming Process on Composite mode I Interlaminar Fracture Toughness


    Beteiligte:
    CHEN Xingyi (Autor:in) / LI Zengshan (Autor:in) / HUANG Xiao (Autor:in) / KOU Zhejun (Autor:in)


    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Interlaminar fracture toughness of carbon/flax fiber hybrid composite

    YUAN Weike / LI Yan / ZHAO Jian | DOAJ | 2022

    Freier Zugriff

    Numerical Analysis Of Interlaminar-Fracture Toughness

    Chamis, C. C. / Murthy, P. L. N. | NTRS | 1988




    On Edge Crack Torsion Test Method to Measure Mode III Interlaminar Fracture Toughness of Composite Laminates

    Suemasu, H. / AIAA / ASME et al. | British Library Conference Proceedings | 1998