The 10Cr13Co13Mo5Ni3W1VE(S280) ultra-high strength stainless steel was subjected to isothermal and constant strain rate compression experiments at deformation temperature of 800-1150 °C, the strain rate of 0.001-10 s–1, and the deformation amount of 70% by using Thermecmaster-Z thermal simulation testing machine. The hot deformation behavior of the steel was analyzed, and the processing maps based on Murty instability criterion were established. The results show that the flow stress of S280 ultra-high strength stainless steel during hot deformation is sensitive to deformation temperature and strain rate. With the increase of strain rate and the decrease of deformation temperature, the flow stress increases significantly. It is determined that the region of instability occurs in the temperature range of 800-1040 °C and strain rate range of 0.06-10 s–1, and the corresponding instability deformation mechanism is mainly flow localization. The desired parameters are 1095-1150 ℃ and 0.001-0.04 s–1 with the plastic deformation mechanism of dynamic recrystallization, and the optimum parameters are around 1125 ℃ and 0.001 s–1.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Hot deformation behavior and processing map of ultra-high strength stainless steel


    Beteiligte:
    LIU Mutong (Autor:in) / ZHONG Ping (Autor:in) / LIU Dabo (Autor:in) / WANG Kelu (Autor:in) / ZHANG Kaiming (Autor:in) / LU Shiqiang (Autor:in)


    Erscheinungsdatum :

    2022




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Deformation behavior of high strength steel sheets

    Oki,T. / Shibata,Z. / Sudo,M. et al. | Kraftfahrwesen | 1981


    Deformation Behavior of High Strength Steel Sheets

    Sudo, M. / Oki, T. / Shibata, Z. | SAE Technical Papers | 1981


    High-strength cryoformed stainless steel cylinders

    Meyer, G.F. / Kesten, M. | Tema Archiv | 1996



    Behavior of corrosion inhibitor on the new ultra high strength steel

    Quintanilla, H. / Inde, A. / Aguilar, A. et al. | Tema Archiv | 2009