Selective electron beam melting (SEBM), which is a powder-bed fusion additive manufacturing technology has unique advantages in the preparation of intermetallic materials with low room temperature plasticity. Recently TiAl alloy parts prepared by SEBM have been successfully used in advanced aeroengines. In this study, crack-free TiAl alloy low-pressure turbine blade simulation parts were prepared by SEBM using Ti-48Al-2Cr-2Nb powder. The tensile properties of the samples at room temperature and the thermal shock resistance of the blades were evaluated. The results indicate that the room temperature tensile strength of TiAl alloy prepared by SEBM can reach 515 MPa after heat treatment, and the elongation after failure is 1.13%. No cracks are found after 120 cycles of thermal shocks at 700 °C tested by the water quenching. The crack perpendicular to the radial direction is appeared in the aerofoil position after 6 times of accelerated thermal shocks tested at 900 °C. Combined with the analysis of crack propagation path and crack fracture, it is determined that the main mechanism of blade component failure under thermal shock conditions is due to the stress concentration caused by the large surface roughness.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Thermal shock failure mechanism of TiAl alloy blade prepared by SEBM


    Beteiligte:
    GAO Runqi (Autor:in) / PENG Hui (Autor:in) / GUO Hongbo (Autor:in) / ZHOU Zhaohui (Autor:in) / DENG Yangpi (Autor:in)


    Erscheinungsdatum :

    2022




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    High Temperature Low Cycle Fatigue Properties and Failure Mechanism of a TiAl Alloy

    DONG Chengli / YU Huichen / JIAO Zehui et al. | DOAJ | 2017

    Freier Zugriff

    Shock Wave Compaction of TiAl

    Gauvin, R. / Brouillette, M. / Canadian Aeronautics and Space Institute | British Library Conference Proceedings | 1994


    Atomic Simulation of Fatigue Crack Growth Mechanism of Single Crystal γ-TiAl Alloy

    ZHANG Ling / LUO Dechun / BAI Xiangxia et al. | DOAJ | 2018

    Freier Zugriff

    Shock-free turbomachinery blade design

    BEAUCHAMP, P. P. / SEEBASS, A. R. | AIAA | 1985


    Shock-free turbomachinery blade design

    Beauchamp, P. P. / Seebass, A. R. | NTRS | 1985