In order to study the relationship of fatigue property、crack growth and organization form of TiAl alloy, the micro crack growth and micro deformation mechanism of single crystal γ-TiAl alloy with an embedded boundary crack under cyclic loading were studied by means of molecular dynamics and velocity loading. Results show that the crack growth process and micro deformation mechanism of single crystal γ-TiAl alloy under cyclic loading were divided into three stages. The mechanical properties are affected by the defects of crack tip lattice distortion,prismatic dislocation slip, Lomer-cottrell dislocation group formation,stacking fault start, deformation twin, etc. and their interaction results in the loading process. The mechanism of crack growth and the mechanism of plastic deformation at different stages were quite different. The research results provide a strong theoretical guidance for improving the performance of γ-TiAlalloys under complex external loading conditions.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Atomic Simulation of Fatigue Crack Growth Mechanism of Single Crystal γ-TiAl Alloy


    Beteiligte:
    ZHANG Ling (Autor:in) / LUO Dechun (Autor:in) / BAI Xiangxia (Autor:in) / RUI Zhiyuan (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    High Temperature Low Cycle Fatigue Properties and Failure Mechanism of a TiAl Alloy

    DONG Chengli / YU Huichen / JIAO Zehui et al. | DOAJ | 2017

    Freier Zugriff

    Statistical Distribution of Fatigue Life for Cast TiAl Alloy

    WAN Wenjuan / HAN Bo / HAN Wei et al. | DOAJ | 2016

    Freier Zugriff



    Fatigue Crack Growth of A356-T6 Cast Aluminum Alloy

    Wigant, C. C. / Stephens, R. I. | SAE Technical Papers | 1988