Methodology of prognostication of thermodynamics properties of melts is presented from the coordinatesof liquidus of diagram of the state in area of equilibria a hard component is solution, on which energies ofmixing of Gibbs are expected in the double border systems of MgO – Al2O3, MgO – SiO2, MgO – CaF2,Al2O3 – SiO2, Al2O3 - CaF2, SiO2 - CaF2. For the areas of equilibrium there is quasibinary connection(MgAl2O4, Mg2SiO4, Al6Si2O13) – a grout at calculations was used equalization of Hauffe-Wagner. Theobtained data comport with literary
THE THERMODYNAMIC PROPERTIES OF MELTS OF DOUBLE SYSTEM MgO – Al2O3, MgO – SiO2, MgO – CaF2, Al2O3 – SiO2, Al2O3 – CaF2, SiO2 – CaF2
2012
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
DOAJ | 2011
|British Library Online Contents | 2018
|Al2O3-SiO2 yu B2O3-Al2O3-SiO2 xi ji qi rong mei zhi yan jiu
TIBKAT | 1964
|Neuartige Effektpigmente basierend auf SiO2- und Al2O3-flakes
Tema Archiv | 1998
|Multilayered Al2O3-SiO2 and TiO2-SiO2 coatings for glazed colored solar thermal collectors
Online Contents | 2005
|