The high temperature deformation behavior of vacuum powder forging FGH95 alloy was studied by Gleeble-3800 thermal simulation testing machine. The hot compression test was carried out at the deformation temperature of 1090-1170 ℃ and the strain rate of 0.01-10 s−1. The flow stress-strain curves under the corresponding conditions were obtained. The effects of deformation conditions on the microstructure evolution of vacuum powder forging FGH95 alloy were analyzed by EBSD. After considering the influence of temperature,strain rate and strain on the flow behavior of the alloy,the Arrhenius equation was selected to establish the constitutive model of vacuum powder forging FGH95 alloy,and the parameters of vacuum powder forging FGH95 alloy were obtained. The relationship between material parameters and strain was fitted and the obtained constitutive equation was verified.The results show that the flow stress of FGH95 alloy prepared by vacuum powder forging process decreases with the increase of temperature and increases with the increase of strain rate. The size of recrystallized grains in the deformed microstructure decreases with the increase of temperature and increases with the decrease of strain rate. The error between the predicted value and the experimental value of the flow stress of the vacuum powder forging FGH95 alloy is 6.33%,and the predicted value is in good agreement with the experimental value.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Flow behavior and microstructure evolution of FGH95 alloy formed by vacuum powder forging


    Beteiligte:
    LI Nan (Autor:in) / CHEN Jingwei (Autor:in) / QU Jinglong (Autor:in) / JIA Jian (Autor:in) / SHENG Liwen (Autor:in) / YANG Shufeng (Autor:in)


    Erscheinungsdatum :

    2024




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Effect of surface integrity evolution on high-temperature fatigue property of FGH95 alloy

    LUO Xuekun / WU Xiaoyan / WANG Kechang et al. | DOAJ | 2020

    Freier Zugriff

    Thermal Simulation Test of AA-FGH95 Superalloy

    WANG Xuqing1 / ZHANG Mincong / LUO Junpeng et al. | DOAJ | 2016

    Freier Zugriff


    The Effect of Forging Conditions on the Flow Behavior and Microstructure of a Medium Carbon Microalloyed Forging Steel

    Van Tyne, Chester J. / Krauss, George / Aloi, Nicholas E. et al. | SAE Technical Papers | 1994


    Theoretical analysis of powder forging

    Dwivedi,S. / Sharan,R. / Lyons,D.W. et al. | Kraftfahrwesen | 1991