The hot deformation behavior of AA-FGH95 superalloy was investigated by hot compressive tests on Gleeble-1500D thermal simulation test machine in different temperatures and strain rates. The true stress-strain curves were obtained, and based on the deformation data, the constitutive equation and processing map of FGH95 superalloy were built. The deformation active energy of AA-FGH95 is Q=695.78 kJ/mol. The results show that the simulated maximum stresses are in agreement with the experimental data, and the average error is about 6%. Based on the processing map, the safety processing parameters of 1070-1100℃ and 0.01-0.001 s-1 are confirmed. When the temperature reached 1100℃, the maximum strain rate increased to 0.5 s-1.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Thermal Simulation Test of AA-FGH95 Superalloy


    Beteiligte:
    WANG Xuqing1 (Autor:in) / ZHANG Mincong (Autor:in) / LUO Junpeng (Autor:in) / PENG Zichao (Autor:in) / SHENG Junying (Autor:in) / YAN Jian (Autor:in)


    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Creep Behaviors of FGH95 Powder Ni-Base Superalloy

    Sugui, T. / Yang, L. / Xiaoming, Z. et al. | British Library Online Contents | 2009


    Flow behavior and microstructure evolution of FGH95 alloy formed by vacuum powder forging

    LI Nan / CHEN Jingwei / QU Jinglong et al. | DOAJ | 2024

    Freier Zugriff

    Effect of surface integrity evolution on high-temperature fatigue property of FGH95 alloy

    LUO Xuekun / WU Xiaoyan / WANG Kechang et al. | DOAJ | 2020

    Freier Zugriff


    Nickel-base superalloy

    Emerald Group Publishing | 1998