As a functional material of burn-resistant titanium alloy, the physical properties of Ti40 alloy were first reported. The chemical compositions of Ti40 alloy ingots by VAR were uniform. The microstructures of Ti40 alloy slab manufactured by HEFF+WPF were uniform. The results show that the room temperature tensile strength of Ti40 alloy is 950 MPa degree. The properties of high temperature heat exposure, creep resistance and lasting time are good at 500 ℃. In the range from room temperature to 600 ℃, Young's modulus and shear modulus are decreased linearly with increasing the temperature, Poisson's ratio is increases slowly as the temperature rises, and linear thermal expansion coefficient and average linear expansion coefficient is increase as the temperature rises.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Thermo-physical Properties and Mechanical Properties of Burn-resistant Titanium Alloy Ti40


    Beteiligte:
    LAI Yunjin (Autor:in) / ZHANG Pingxiang (Autor:in) / ZHANG Saifei (Autor:in) / WANG Kaixuan (Autor:in) / LEI Qiang (Autor:in) / XIN Shewei (Autor:in) / ZHENG Yongjian (Autor:in) / TAN Qiming (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Constitutive model of Ti40 alloy sheet based on DIC measurement

    Jiang,J. / Wang,H. / Gu,J. et al. | Kraftfahrwesen | 2013


    Constitutive Model of Ti40 Alloy Sheet Based on DIC Measurement

    Wang, Houmin / Jiang, Jianhua / Gu, Junhai | SAE Technical Papers | 2013


    Surface integrity of burn resistant titanium alloy following machining

    Novovic, D. / Aspinwall, D.K. / Dewes, R.C. et al. | Tema Archiv | 2003


    Improvement of thermo-mechanical properties of basalt fiber using heat resistant polymeric coatings

    Shayed, M. A. / Hund, R. D. / Cherif, C. | British Library Online Contents | 2014


    The Effects of Thermo-Mechanical Treatment on the Properties of 2519 Aluminium Alloy

    Lin, G. Y. / Zhang, Z. F. / Lin, Q. Q. et al. | British Library Conference Proceedings | 2007