NiO,Er2O3,Yb2O3,Y2O3 and ZrO2 powders were used as raw materials to prepare composite ceramic materials by the method of high temperature solid phase synthesis. The specific heat, thermal diffusion coefficient, thermal conductivity and other thermal physical properties of the composite ceramic materials were studied and compared with the traditional 8YSZ thermal barrier coating materials. The crystal structure and phase composition were tested by XRD. The results show that after NiO,Er2O3,Yb2O3,Y2O3 and ZrO2 co-doping, the thermal diffusion coefficient is 0.36-0.56 mm2/s, which is 20% lower than that of YSZ from room temperature to 1500 ℃,the thermal conductivities is 1.45-1.55 W/(m?K), which is 18% lower than that of YSZ from room temperature to 1500 ℃,2EYNYSZ material has single phase structure, and 1500 ℃ heat-treatment does not occur phase transition within 100 h.
Influence of ternary co-doping on thermo-physical properties of YSZ thermal barrier coatings
2019
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Microstructure and thermo-physical properties of plasma sprayed LaTi2Al9O19 thermal barrier coatings
Online Contents | 2013
|AIAA | 2014
|Thick Thermal Barrier Coatings
British Library Conference Proceedings | 1994
|Thick thermal barrier coatings
Kraftfahrwesen | 1994
|Thick thermal barrier coatings
Kraftfahrwesen | 1993
|