HIPed FGH96 superalloy prepared by AA powder was used as the research object, and the PPB precipitations and microstructures before and after different hot deformations were studied. The results show that PPB precipitates with circular distribution can be seen in HIPed FGH96 superalloy, and the coarse strip prime γ′ phase with circular chain distribution is one of the main characters of PPB. After hot deformation, the PPB in FGH96 superalloy is deformed and broken, the recrystallization grains are refined and twisted, and the grain misorientation becomes smaller. With the increase of deformation temperature and hot deformation, and the decrease of deformation rate, the deformation and fragmentation of PPB precipitates are more significant, the size of the primary residual γ′ phase becomes smaller, and the volume becomes less. The increase of deformation temperature and hot deformation, and the decrease of deformation rate are beneficial to reduce or even eliminate PPB precipitations.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Hot Deformation on PPB Precipitations and Microstructure in P/M Superalloy FGH96


    Beteiligte:
    LIU Changkui (Autor:in) / WEI Zhenwei (Autor:in) / ZHANG Jiaqing (Autor:in) / ZHENG Zhen (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Interfacial reaction between mullite-based inclusions and PM superalloy FGH96

    ZHANG Yibo / ZHENG Liang / XU Wenyong et al. | DOAJ | 2022

    Freier Zugriff


    Effect of Deforming Temperature and Strain on Abnormal Grain Growth of Extruded FGH96 Superalloy

    WANG Chaoyuan / DONG Yunpeng / SONG Xiaojun et al. | DOAJ | 2016

    Freier Zugriff

    Prior Particle Boundary of PM FGH96 Superalloy and Its In-situ High-cycle Fatigue at Elevated Temperature

    ZHOU Jingyi / LIU Changkui / ZHAO Wenxia et al. | DOAJ | 2017

    Freier Zugriff

    Microstructures and Properties of FGH96/DD6 Joints Brazed at Vacuum Pressure State

    ZOU Wenjiang / CHEN Bo / CHENG Yaoyong et al. | DOAJ | 2017

    Freier Zugriff