The influence of different grades of prior particle boundary (PPB) in PM FGH96 superalloy during high-cycle fatigue test at 550 ℃ was investigated by the in-situ fatigue test in SEM. The results show that the PPB in P/M FGH96 superalloys by plasma rotating electrode process (PREP) + hot isostatic press (HIP) is constituted of large size γ' and carbide. There are no significant effect on the initiation and propagation of high cycle fatigue crack in different grades of PPB. Crack initiation is initiated in the grain interior, and the propagation is transgranular or intergranular, which is influenced by the angle between the grain boundary and the stress axis. In the fast crack growth zone and the transient zone, the fracture characteristics of serious grade PPB FGH96 superalloy are transgranular and along PPB globular surfaces.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Prior Particle Boundary of PM FGH96 Superalloy and Its In-situ High-cycle Fatigue at Elevated Temperature


    Beteiligte:
    ZHOU Jingyi (Autor:in) / LIU Changkui (Autor:in) / ZHAO Wenxia (Autor:in) / ZHENG Zhen (Autor:in) / ZHONG Yan (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Interfacial reaction between mullite-based inclusions and PM superalloy FGH96

    ZHANG Yibo / ZHENG Liang / XU Wenyong et al. | DOAJ | 2022

    Freier Zugriff

    Effect of Deforming Temperature and Strain on Abnormal Grain Growth of Extruded FGH96 Superalloy

    WANG Chaoyuan / DONG Yunpeng / SONG Xiaojun et al. | DOAJ | 2016

    Freier Zugriff


    Effect of Hot Deformation on PPB Precipitations and Microstructure in P/M Superalloy FGH96

    LIU Changkui / WEI Zhenwei / ZHANG Jiaqing et al. | DOAJ | 2018

    Freier Zugriff

    Analog-Circuit Model of FGH96 Superalloy Hot Deformation Behaviors Based on Artificial Neural Network

    Liu, Y.-h. / Li, F.-g. / Li, C. et al. | British Library Online Contents | 2005