Corrosion mechanism and rate of different chemical composition and structural condition of wheel steel were investigated. It was shown that “white layers”, variation in grain size and banding of wheel steel structure results in corrosion rate. Microstructure of steel from different elements of railway wheels after operation with corrosion was investigated. Wheel steel with addition of vanadium corroded more quickly than steel without vanadium. Non-metallic inclusions are the centre of corrosion nucleation and their influence on corrosion depends on type of inclusion. Mechanism of corrosion of wheel steel corrosion was discussed.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Some peculiarities of corrosion of wheel steel


    Beteiligte:
    Alexander SHRAMKO (Autor:in) / Alfred KOZLOWSKY (Autor:in) / Elena BELAJA (Autor:in) / Yuriy PROIDAK (Autor:in) / Sofia PINCHUK (Autor:in) / Svetlana GUBENKO (Autor:in)


    Erscheinungsdatum :

    2009



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Some Peculiarities of Wheel/Rail Interaction in Passing throughSmall-Radius Curves

    Grigorenko, V. G. / Doronin, V. I. / All-Russian Railway Research Institute | British Library Conference Proceedings | 1999


    Some peculiarities about water

    Engineering Index Backfile | 1900


    Peculiarities of traction forces in wheel/rail contact area

    Š. Mikaliūnas / G. Bureika | DOAJ | 2002

    Freier Zugriff

    Peculiarities of traction forces in wheel/rail contact area

    Gintautas Bureika / Šarūnas Mikaliūnas | DOAJ | 2002

    Freier Zugriff

    Channels and drops -- Some peculiarities

    Peter, Y. | Engineering Index Backfile | 1964