Three different proportions of TA15 and Ti2AlNb alloy powde were premixed and thin-walls with proportions of 40%TA15+60%Ti2AlNb, 50%TA15 +50% Ti2AlNb and 60%TA15+40%Ti2AlNb (mass fraction) were prepared by using laser melting deposition process. The composition, microstructure and mechanical properties of the three thin-walls were analyzed. The results indicate that the compositions of all the three kinds of alloys are uniform. The alloy appears as basketweave microstructure with acicular α phase and α2 phase distributing within primary β/B2 grain. Tensile strength of the three kinds of alloys are 1108 MPa and 1071 MPa, 1105 MPa, and elongation are 3.0%, 2.2% and 3.8% respectively; Tear ridge along α2 phases is visible on tensile fracture surface, and the fracture mode is subject to cleavage fracture.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Microstructure and Mechanical Properties of Laser Melting Deposited TA15+Ti2AlNb Alloys


    Beteiligte:
    LIU Yantao (Autor:in) / ZHANG Yongzhong (Autor:in) / CHEN Yiqiang (Autor:in) / TANG Yangjie (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Effect of composition on microstructure and mechanical properties of TA15 titanium alloy

    SUI Nan / CAO Jingxia / HUANG Xu et al. | DOAJ | 2019

    Freier Zugriff



    Research progress of microstructure transformation and kinetics in Ti2AlNb-based alloy

    CHENG Jianwen / RAO Qunli / LI Jinfu et al. | DOAJ | 2022

    Freier Zugriff

    Influence of laser shock peening times on microstructure and hardness of TA15 titanium alloy

    Ying, Z. / Bowen, F. / Wei, G. et al. | British Library Online Contents | 2014