Static tension test allows characterization of material strength properties. This simple test provides input data for numerical calculation of structural components made of the tested alloy. Elastic, plastic and failure behavior of the structural component in question is simulated, using, for example, the FEM package, based on parameters obtained as the result of tensile testing. When using the results of the tensile test for modeling the material failure it is important to estimate correctly plastic strain corresponding to failure. It is common practice to use elongation of the specimen gage part for the calculation of failure strain. On the other side, the most popular ductile failure criterion used by engineers performing numerical simulation of the material’s behavior relies on the equivalent plastic strain as the criterial quantity. Those two parameters can differ significantly. In order to calculate the equivalent plastic strain correctly, we have to remember about strain localization (necking) appearing during tensile tests and take into account the fact that during tensile testing we have three non-zero strain tensor components. Ignoring this fact, and using only elongation as the criterial quantity can lead to enormous simulation error. This error is analyzed in this paper for nickel based superalloy tested at elevated temperatures.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Calibration of the Ductile Failure Criterion for Nickel-Based Superalloys taking into Account the Localization of the Strain


    Beteiligte:
    Madejski Bartosz (Autor:in) / Socha Grzegorz (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Nickel-Based Superalloys

    Satyanarayana, D. V. V. / Eswara Prasad, N. | Springer Verlag | 2016


    Nickel-Based Superalloys

    Shih, Tom I-P. / Yang, Vigor | AIAA | 2014


    Predicting Forming Limit Curve Using a New Ductile Failure Criterion

    Mallick, Pankaj / Sheng, ZiQiang | SAE Technical Papers | 2017


    Thermophysical Properties of Nickel-Based Superalloys

    SanSoucie, Michael P. / Rogers, Jan R. / Xiao, Xiao et al. | NTRS | 2018


    Unified plastic yield criterion for ductile solids.

    MAITRA, M. / MAJUMDAR, K. / DAS, A. | AIAA | 1973