LiCoO2 coated with graphene and PSS:PEDOT(GP-LCO)is synthesized by a facile and scalable method. The structure and morphology of LiCoO2(LCO)and GP-LCO have been investigated by X-ray diffraction(XRD)and scanning electron microscopy(SEM). Transmission electron microscopy(TEM)further demonstrate the existence of graphene and PSS:PEDOT. The electrochemical properties of the composites are investigated by cyclic voltammetry and AC impedance measurements, which show that the conductive film of graphene(1%)and PSS:PEDOT(2%)on the surface significantly decreases the charge transfer resistance and improves the cycle stability of LiCoO2. Galvanostatic charge-discharge test reveals that with only 2% Super P as conductive additive, the GP-LCO delivers a capacity of 173.9 mAh/g at 0.1 C and 118.0 mAh/g at 10 C, which are higher than the pristine LCO in the potential range of 3.0-4.5 V(vs. Li/Li+). Moreover, it is clearly noticed that the GP-LCO exhibits a capacity retention of 76.6% after 100 cycles at 0.1C, while the LCO only presents a capacity retention of 41.1%.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Preparation of LiCoO2 composite coated with graphene and PEDOT∶PSS with enhanced electrochemical properties at high voltage for lithium-ion batteries


    Beteiligte:
    WANG Jixian (Autor:in) / PENG Sikan (Autor:in) / WANG Chen (Autor:in) / NAN Wenzheng (Autor:in) / LIU Mingliang (Autor:in) / YAN Shaojiu (Autor:in) / DAI Shenglong (Autor:in)


    Erscheinungsdatum :

    2023




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt