Ceramic cores provide complex internal cavity structures in the investment precision castings of hollow blades for aero-engine. The silica/mullite ceramic cores were fabricated by hot injection molding, adding fused mullite powders with different particle sizes as mineralizers. The particle size of mullite mineralizers on the crystallization and properties of ceramic cores was investigated in the paper. The result shows that the mullite mineralizers promote the crystallization of cristobalite in ceramic cores, and finer mullite powders can further improve the heterogeneous nucleation, and generate larger quantities of cristobalite. Mullite mineralizers with large particle size can lead to low sintering degree, poor mechanical properties and creep resistance of ceramic cores. While the particle size of mullite mineralizers is too small, the core contains too much quartzite crystal phase, and the microcrack occurs during the phase transformation during cooling, which also causes the deterioration of the strength at room temperature and the high temperature deformation resistance ability. The ceramic cores with mullite powders in particle size of 19 μm show excellent comprehensive performance, with linear shrinkage of 0.65%, porosity of 31.8%, room temperature strength of 17.8 MPa, high temperature creep deformation of 0.4 mm, and leaching rate of 0.06 g/min.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Fabrication and properties of silica-based ceramic cores modified by mullite powders with different particle sizes


    Beteiligte:
    WU Xiaofei (Autor:in) / LI Xin (Autor:in) / XU Xiqing (Autor:in) / NIU Shuxin (Autor:in) / FAN Hongna (Autor:in) / YANG Xiaowei (Autor:in)


    Erscheinungsdatum :

    2021




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt





    Reactive, Mechanically Alloyed Al · Mg Powders with Customized Particle Sizes and Compositions

    Aly, Yasmine / Hoffman, Vern K. / Schoenitz, Mirko et al. | AIAA | 2013


    Mechanical Properties of mullite

    Ohnishi,H. / Kawanami,T. / Miyazaki,K. et al. | Kraftfahrwesen | 1986


    Effects of Starch on Properties of Alumina-based Ceramic Cores

    LI Fengguang / TANG Shiyan / LIU Fuchu et al. | DOAJ | 2016

    Freier Zugriff

    Homogeneous precipitation and thermal phase transformation of mullite ceramic precursor

    Satoshi, S. / Contreras, C. / Juarez, H. et al. | British Library Online Contents | 2001