In order to improve the poor leachability of alumina-based ceramic cores, different amount of starch was added to the specimens as pore former. Alumina-based ceramic cores were prepared by hot injection technology using corundum powder as base material, paraffin wax and beeswax as plasticizer, silica powder and magnesium oxide powder as mineralizing agent, wherein the parameters of the hot injection process were as follows:temperature of the slurry was 90℃, hot injection pressure was 0.5 MPa and holding time was 25 s. The effects of starch content on the properties of alumina-based ceramic cores were studied and discussed. The results indicate that during sintering period, the loss of starch in the specimens makes porosity of the alumina-based ceramic cores increase. When starch content increases, the room-temperature flexural strength of the ceramic cores reduces and the apparent porosity increases; the volatile solvent increases and the bulk density decreases. After being sintered at 1560℃ for 2.5 h, room-temperature flexural strength of the alumina-based ceramic cores with starch content of 8%(mass fraction) is 24.8 MPa, apparent porosity is 47.98% when the volatile solvent is 1.92 g/h and bulk density is 1.88 g/cm3, the complex properties are optimal.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effects of Starch on Properties of Alumina-based Ceramic Cores


    Beteiligte:
    LI Fengguang (Autor:in) / TANG Shiyan (Autor:in) / LIU Fuchu (Autor:in) / FAN Zitian (Autor:in)


    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Glazed Ceramic Sheet 95% Alumina

    SAE Technical Papers | 1995


    GLAZED CERAMIC SHEET 95% Alumina

    SAE Technical Papers | 1991


    GLAZED CERAMIC SHEET 95% Alumina

    SAE Technical Papers | 1993



    GLAZED CERAMIC SHEET 95% Alumina Base

    SAE Technical Papers | 1972