Vacuum brazing of K465 superalloy was carried out by using Co45NiCrWB cobalt-base filler metal at 1220 ℃ for different holding time, and the joint clearance was 0.5 mm pre-filled with FGH95 nickel-base superalloy powder. The effect of the structural constitution of brazed different holding time of temperature on the brazed joint microstructure and properties. The results show that the brazing seam is composed of alloy powder particles and borides among them. It is two-phase structure of γ and γ' with a few small blocks of borides in the powder particles, and there exists phases rich in Cr, W and Nb elements. The powder particles are growing along the holding time during the brazing process, while their combination is expanded. It is good for stress rapture properties of joints that borides was fine in brazing seam with more superalloy powder and proper holding time. And the joints brazed for 30-60 min show higher stress rapture properties.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Microstructure and Mechanical Properties of Wide-gap Brazed Joints of K465 Alloy Using Cobalt-base Brazing Alloy


    Beteiligte:
    PAN Hui (Autor:in) / ZHAO Haisheng (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt