Self-corrosion and pitting corrosion of 7B04 aluminum alloy at different environment conditions were studied by electrochemical test with simulating surface coating damage on 7B04 aluminum alloy. The forming conditions of pitting corrosion after contacting 7B04 aluminum alloy with TA15 titanium alloy were analyzed by finite element method which was based on the mathematical model of galvanic corrosion. The results indicate that the pitting potential of 7B04 aluminum alloy is influenced by Cl- concentration and pH value. Pitting corrosion of 7B04 aluminum alloy in self-corrosion condition can occur in neutral solution(mass fraction of NaCl>5%) or in acidic solution(mass fraction of NaCl=3.5%). The potential rises when 7B04 aluminum alloy contacts with TA15 titanium alloy which results in the occurrence probability of pitting corrosion. The occurrence probability of pitting corrosion is increased. The pitting corrosion of 7B04 aluminum alloy initiates and propagates when the area ratio of cathode and anode is greater than 40 in neutral solution(mass fraction of NaCl=3.5%). The potential of 7B04 aluminum alloy decreases slowly with the increase of the distance between cathode and anode, and the decline of the potential is not over 2 mV at distance within 10 m.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Influence and Simulation Study of Surface Coating Damage on Pitting Corrosion of 7B04 Aluminum Alloy


    Beteiligte:
    WANG Chenguang (Autor:in) / CHEN Yueliang (Autor:in) / ZHANG Yong (Autor:in) / BIAN Guixue (Autor:in)


    Erscheinungsdatum :

    2016




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Corrosion Behavior of 7B04 Al-alloy in Simulated Marine Atmospheric Environment

    WANG Chenguang / CHEN Yueliang / ZHANG Yong et al. | DOAJ | 2017

    Freier Zugriff

    Constitutive equations of high strength aluminum alloy sheet 7B04-T6 under warm tension

    Zhi, Z. / Lihui, L. / Tao, L. et al. | British Library Online Contents | 2009


    Effect of flap peening on stress corrosion cracking resistance of 7B04-T6 alloy

    HE Wang / WANG Yanli / WANG Yanan et al. | DOAJ | 2020

    Freier Zugriff

    Evolution of Pitting Corrosion in a 2024-T3 Aluminum Alloy

    Burynski, R. M. / Chen, G.-S. / Wei, R. P. | British Library Online Contents | 1995


    Evolution of Pitting Corrosion in a 2024-T3 Aluminum Alloy

    Burynski, R. M. / Chen, G.-S. / Wei, R. P. et al. | British Library Conference Proceedings | 1995