To investigate the failure behavior of open-hole carbon fiber reinforced plastics (CFRP) under the circumstance of tensile loading, three-dimensional Hashin failure criteria was adopted to predict damage initiation, and a stiffness degradation method based on progressive damage theory was proposed to assess the damage evolution. The subroutine UMAT was developed to numerically analyze the loading capacity and failure behavior of open-hole CFRP laminates under tension. The numerical prediction of ultimate loading capacity and failure procedure are compared with the experimental data, and the results are indentical. Therefore, the effectiveness and accuracy of the proposed method are validated.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Progressive Damage Based Failure Analysis of Open-hole Composite Laminates under Tension


    Beteiligte:
    LI Rupeng (Autor:in) / CHEN Lei (Autor:in) / LIU Xueshu (Autor:in) / ZENG Xiangqian (Autor:in) / GAO Hang (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Continuum Damage Mechanics Models for the Analysis of Progressive Failure in Open-Hole Tension Laminates

    Song, K. / Li, Y. / Rose, C. et al. | British Library Conference Proceedings | 2011



    Progressive Damage and Failure Prediction of Open Hole Tension and Open Hole Compression Specimens

    Joseph, Ashith P K / Waas, Anthony M. / Ji, Wooseok et al. | AIAA | 2015


    Progressive Damage and Failure Prediction of Open Hole Tension and Open Hole Compression Specimens (AIAA 2015-0466)

    Joseph, Ashith P. K. / Waas, Anthony M. / Ji, Wooseok et al. | British Library Conference Proceedings | 2015