The effect of Mo content on microstructure and mechanical properties of IN718 alloy after standard heat treatment was investigated by means of optical microscopy(OM), scanning electron microscopy(SEM), transmission electron microscopy(TEM) and energy dispersive spectrometer(EDS). The results show that Mo significantly affects the intergranular precipitation. The amount of δ phase is decreased by the increase of Mo addition up to 4.00%. However, δ phase is inhibited thoroughly but Laves phase begins to precipitate at grain boundaries when Mo addition is higher than 5.50%, and the precipitation of Laves phase is increased by the increase of Mo content. Both the disk-shaped γ″ phase and spherical γ′ phase are precipitated in γ matrix grain in all of the alloys with the Mo additions ranging from 2.8% up to 7.5%, and there are no other second precipitates. Mo has no obvious effect on the number of the precipitation of γ″ phase and γ′ phase, but their sizes are decreased with the increase of Mo addition. Mo slightly reduces the tensile strength of IN718 alloy at room temperature and yield strength at 680 ℃. At room temperature, Mo addition lower than 5.5% has no evident effect on the tensile ductility, while the ductility is remarkably decreased when Mo addition is 7.50%. At 680 ℃, the ductility is enhanced gradually as Mo addition increases. Mo obviously improves the stress rupture life of IN718 alloy at 680 ℃ and 725 MPa. The life of the alloy with 7.50% Mo is about 1.5 times as long as that of the alloy with 2.8% Mo. Mo has no obvious effect on the tress rupture ductility.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Mo content on Microstructure and Mechanical Properties of IN718 Alloy


    Beteiligte:
    HAN Dawei (Autor:in) / SUN Wenru (Autor:in) / YU Lianxu (Autor:in) / LIU Fang (Autor:in) / ZHANG Bin (Autor:in) / HU Zhuangqi (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    INVESTIGATION OF MECHANICAL PROPERTIES AND STRUCTURE OF IN718 ALLOY PRODUCED BY 3D-PRINTING

    Никита Олегович Коваль / Оксана Сергеевна Воденникова | DOAJ | 2020

    Freier Zugriff

    IN718 Additive Manufacturing Properties and Influences

    M. D. Lambert / A. M. Adler | NTIS | 2014



    Effect of Fe content on microstructure and mechanical properties of Al-Mg-Si alloy

    LIU Hui / FU Yilei / CHEN Zongqiang et al. | DOAJ | 2023

    Freier Zugriff