Fracture endurance limit is one of the main parameters used in calculating the strength of surface hardened parts. The influence of various operational factors along with hardening should be taken into account in predicting this parameter. Prediction of the endurance limit under stress concentration was carried out according to the criterion that takes into account the influence of residual stresses on the surface of the dangerous section of a hardened part, as well as the criterion of the average integral residual stresses over the thickness of the hardened surface layer equal to the critical depth of a non-propagating fatigue crack. The effect of surface hardening on the endurance limit was analyzed taking into account such operational factors as the type of deformation, working temperature, the asymmetry of the loading cycle of specimens made of steels and aluminum alloys. Fatigue tests of cylindrical specimens with circular notches of a semicircular profile were carried out under torsion, bending and tension-and-compression. It was established that the use of the criterion of the average integral residual stresses is quite a good indicator of the effect of surface hardening on the fracture endurance limit taking into account the operational factors studied.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Prediction of endurance limit of hardened parts with account of operational factors


    Beteiligte:
    V. F. Pavlov (Autor:in) / V. A. Kirpichev (Autor:in) / P. E. Kiselev (Autor:in) / A. A. Shvetsova (Autor:in)


    Erscheinungsdatum :

    2018




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Endurance Limit Modifying Factors for Hardened Machined Surfaces

    Shareef, Iqbal / Hasselbusch, Michael D. | SAE Technical Papers | 1996


    Grinding out hardened parts

    Luetjens,P. / Mushardt,H. / Schleifring,DE | Kraftfahrwesen | 2004


    Titanium parts can be hardened

    British Library Online Contents | 1998


    Titanium parts can be hardened

    Online Contents | 1998


    PRESSURE-HARDENED SHEET FORMED PARTS WITH DIFFERENT

    SCHNAPP STEFAN / SITTENBERGER MARTIN | Europäisches Patentamt | 2022

    Freier Zugriff