The aim of this study is to investigate the effect of ultrasonic treatment on the microstructural and mechanical properties of A356 aluminum al-loy. Ultrasonic treatment was applied to 2 kg and 4 kg molten metals at different melting temperatures (700 oC, 720 oC and 740 oC) for different durations (0, 60, 180 and 300 seconds). Bifilm indices of the samples were also measured after all parameters were tested. The ultimate tensile strength (UTS) and elongation values were used to calculate the Quality Index (QI) of the samples. According to the results, the amount of liquid metal directly affects the the ultrasonic intensity that is produced during the treatment. Maximum UTS and elongation results were determined at 720 oC during 300 seconds for 4 kg casting. Minimum bifilm density val-ue was measured at the same ultrasonic temperature and time.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Effect of Ultrasonic Treatment Parameters on Microstructural and Mechanical Properties of A356 Aluminum Alloy


    Beteiligte:
    Kazım Önel (Autor:in) / Esra Dokumacı (Autor:in) / Uğur Aybarç (Autor:in)


    Erscheinungsdatum :

    2020




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    High temperature solutionizing and mechanical properties of the A356 aluminum casting alloy

    Takaai, T. / Nakayama, Y. / Ohnishi, N. et al. | Tema Archiv | 1996


    Copper Effect on the Ultrasonic Fatigue Life of A356 Aluminum Alloy Under Variable Humidity Levels

    Li, Wenkai / Engler-Pinto, Carlos / Su, Xuming et al. | British Library Conference Proceedings | 2018


    Copper Effect on the Ultrasonic Fatigue Life of A356 Aluminum Alloy Under Variable Humidity Levels

    Engler-Pinto, Carlos / Li, WENKAI / Su, Xuming et al. | SAE Technical Papers | 2018


    The effect of solidification time on the mechanical properties in a cast A356-T6 aluminum alloy

    Boileau,J.M. / Zindel,J.W. / Allison,J.E. et al. | Kraftfahrwesen | 1997


    The Effect of Solidification Time on the Mechanical Properties in a Cast A356-T6 Aluminum Alloy

    Boileau, J. M. / Zindel, J. W. / Allison, J. E. et al. | British Library Conference Proceedings | 1997