The surface integrity of carburized M50NiL steel was studied by optical microscopy, scanning electron microscopy (SEM), atomic force microscopy (AFM), microhardness tester and residual stress tester. The fatigue properties of the two specimens were measured by the rotational bending fatigue test, and the fatigue test results were simulated and analyzed. The results show that the rotation bending fatigue of carburized M50NiL steel is originated in the sub-surface in the ideal case without considering the surface processing defects. The surface stress concentration factor produced by general grinding causes the fatigue source to be moved from the surface to the sub-surface. Precise grinding improves the surface quality by optimizing the grinding process, effectively restrains the stress concentration of the working surface, and returns the fatigue source from the surface to the sub-surface. The maximum rotary bending fatigue life can be increased by 30 times and the average is 15 times.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Surface Integrity Characteristics and Fatigue Failure Mechanism of Carburized M50NiL Steel


    Beteiligte:
    LOU Yanzhi (Autor:in) / LI Chunzhi (Autor:in) / LI Xudong (Autor:in) / XIE Xiaochang (Autor:in) / ZHAO Zhenye (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Failure Mechanism of Contact Fatigue of Surface Super-hardened M50NiL Steel

    LUO Qinghong / ZHAO Zhenye / HE Ziqiang et al. | DOAJ | 2017

    Freier Zugriff



    Surface Fatigue Tests Of M50NiL Gears And Bars

    Townsend, Dennis P. / Bamberger, Eric N. | NTRS | 1994


    Vacuum carburizing of M50NiL

    MORRAL, J. / LAW, C. | AIAA | 1990