Aircraft aluminum alloy is easy to initiate pitting corrosion in the service environment, the pitting corrosion topography characteristics could directly affect the fatigue mechanical property of structure material. In order to obtain the pitting corrosion topography characteristics of LC4 aluminum alloy in the service environment, the accelerated corrosion test was carried out along the accelerated corrosion test environment spectrum which imitated the service environment spectrum, and the corrosion topography characteristic parameters of corrosion pit depth H,corrosion pit surface length L and corrosion pit surface width W were defined respectively. During the corrosion test process,the three parameters of typical corrosion pit were successively measured in different equivalent corrosion years for obtaining the corrosion pit damage size data, then the data were analysed through the statistics method and fractal theory. Further more in order to gain the pit topography characteristics in the same equivalent corrosion year and the topography evolution laws during different equivalent corrosion years were gained. The analysis results indicate that LC4 aluminum alloy corrosion pit topography characteristics in the service environment include the following:firstly, the pit topography characteristic parameters conform to the lognormal distributions in the same equivalent corrosion years; secondly,the pit topography characteristic parameters gradually reflect the fractal feature in accordance with the equivalent corrosion year increment, and the pits tend to be shallow, long and moderate wide topography character.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Pitting Corrosion Topography Characteristics and Evolution Laws of LC4 Aluminum Alloy in Service Environment


    Beteiligte:
    LIU Zhiguo (Autor:in) / LI Xudong (Autor:in) / MU Zhitao (Autor:in)


    Erscheinungsdatum :

    2017




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Evolution of Pitting Corrosion in a 2024-T3 Aluminum Alloy

    Burynski, R. M. / Chen, G.-S. / Wei, R. P. | British Library Online Contents | 1995


    Evolution of Pitting Corrosion in a 2024-T3 Aluminum Alloy

    Burynski, R. M. / Chen, G.-S. / Wei, R. P. et al. | British Library Conference Proceedings | 1995


    Laser repair method for pitting corrosion damages of aluminum alloy airplane skin

    DONG SHIYUN / SONG CHAOQUN / YAN SHIXING et al. | Europäisches Patentamt | 2020

    Freier Zugriff

    Characterization of pitting corrosion in bare and sol-gel coated aluminum 2024-T3 alloy

    Voevodin, N. / Jeffcoate, C. / Simon, L. et al. | Tema Archiv | 2001


    Influence and Simulation Study of Surface Coating Damage on Pitting Corrosion of 7B04 Aluminum Alloy

    WANG Chenguang / CHEN Yueliang / ZHANG Yong et al. | DOAJ | 2016

    Freier Zugriff