The new generation high-strength steel sheet has been widely used to reduce the vehicle weight. In this study, the mechanical, metallurgical, and fatigue behavior of the resistance spot-welded joints of high strength steel sheets were experimentally investigated. The Dual-Phase (DP) 800 and Twinning-Induced Plasticity (TWIP) 1000 steel sheets were joined together in three different nugget diameters. The welding current was parameterized to create three different nugget diameters. Hence, four groups of welded combining combinations were obtained. The tensile shear test was applied to the samples to study the effects of weld nugget diameter and different welded joint combination in terms of the joint strength. For long fatigue life tests, six test samples were prepared for each test series; in total, 24 tests have been conducted, in which S-N curves of the samples were extracted. Finally, the effect of different nugget diameters on the fatigue life of the welded joint combinations was investigated.
Mechanical and Fatigue Behavior of Resistance Spot Welded Dual-Phase and Twinning-Induced Plasticity Steel Joints
J. Aerosp. Eng.
Journal of Aerospace Engineering ; 35 , 3
2022-05-01
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Fatigue behavior of spot welded high strength steel joints
Kraftfahrwesen | 1981
|Fatigue Behavior of Spot Welded High Strength Steel Joints
SAE Technical Papers | 1981
|Fatigue Strength of Spot Welded Joints in a HSLA Steel
SAE Technical Papers | 1981
|Fatigue strength of spot welded joints in a HSLA steel
Kraftfahrwesen | 1981
|Fatigue Life Prediction On Complex Spot Welded Joints
SAE Technical Papers | 1997
|