Aging of asphalt binders causes the changes in the microstructure of the asphalt binders, consequently, in the mechanical properties. In this study, aging of short-term and long-term was tested on both base and modified asphalt binders using rotating thin film oven (RTFO) and pressure ageing vessel (PAV), respectively. The changes in the nano-mechanical properties were measured using atomic force microscope (AFM) technology. The results indicated: (1) the nano-adhesive forces from AFM were increased for both base and modified asphalt binders after RTFO aging; and (2) the nano-adhesive force was reduced for both base and modified binder, but the former was reduced higher than the later after PAV aging.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Nano-Scaled Mechanical Properties of Asphalt Binders Caused by Aging


    Beteiligte:
    Liu, Ben (Autor:in) / Chen, Jianxin (Autor:in) / Shen, Junan (Autor:in) / Song, Xuyan (Autor:in)

    Kongress:

    2015 International Symposium on Frontiers of Road and Airport Engineering ; 2015 ; Shanghai, China



    Erscheinungsdatum :

    22.10.2015




    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Nano scale aging characterization of carbon nanotube modified asphalt binders

    Mamun, A. A. / Arifuzzaman, Md. / Taha, R. | TIBKAT | 2018


    Oxidative Aging of Asphalt Binders in Hot-Mix Asphalt Mixtures

    Morian, Nathan / Hajj, Elie Y. / Glover, Charles J. et al. | Transportation Research Record | 2011




    Pressure Aging Vessel and Low-Temperature Properties of Asphalt Binders

    Teshale, Eyoab Zegeye / Moon, Ki-Hoon / Turos, Mugurel et al. | Transportation Research Record | 2011