The Composite are material consists of two or more materials which combine macroscopically, for now the strength of the material, it must be test with various method which is represented by the specimen. On this paper will research about material sandwich Composite with flexural three-point bending and flatwise compressive test method. In manufactured generally Composite using vary method. Usually manufacturing uses hand lay-up, vacuum bagging, VARI method and other. In this research author will be use VARI method, the reason is VARI method has a low-cost process and more efficient. In this experiment was carried out on sandwich Composite using carbon fiber unidirectional 0°, with aramid honeycomb core. Specimen and testing will be follow ASTM C365 standard which is flatwise testing standard, for specimen with lycal resin the results average is 56089.6 N Maximum load, 26.68 MPa Compressive of strength, 5.04 moduli of elasticity 5.04 MPa, while for specimen with Vinyl Ester resin the results average is 56089.6 MPa Maximum load, 26.68 MPa Compressive of the core strength, 5.04 MPa moduli of elasticity and Flexural three-point banding will be follow ASTM C393 standard which is Flexural testing standard. The Results of the specimen using Vinyl Ester resin is 1029.14 N maximum load, 13.78 MPa Facing stress, 861.94 moduli of elasticity.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Analysis of mechanical properties sandwich composite honeycomb-unidirectional with matrix Vinyl Ester using VARI method


    Beteiligte:
    Ramadhan, Muhammad Farhan (Autor:in) / Muzayadah, Nurul Lailatul (Autor:in) / Nugroho, Afid (Autor:in) / Rahmadi, Awang (Autor:in) / Jaya, Kukuh Indra (Autor:in) / Aritonang, Rian Suari (Autor:in) / Kurniawan, Farohaji (Herausgeber:in) / Kurniawati, Frida (Herausgeber:in) / Bahri, Sayr (Herausgeber:in) / Santosa, Cahya Edi (Herausgeber:in)

    Kongress:

    THE 8TH INTERNATIONAL SEMINAR ON AEROSPACE SCIENCE AND TECHNOLOGY – ISAST 2020 ; 2020 ; Bogor, Indonesia


    Erschienen in:

    Erscheinungsdatum :

    13.09.2021


    Format / Umfang :

    12 pages





    Medientyp :

    Aufsatz (Konferenz)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Analysis of mechanical properties sandwich composite honeycomb-unidirectional with matrix Vinyl Ester using VARI method

    Ramadhan, Muhammad Farhan / Muzayadah, Nurul Lailatul / Nugroho, Afid et al. | TIBKAT | 2021


    Effect of post curing treatment on tensile properties of glass fibre/lycal composite and glass fibre/vinyl ester composite with VARI manufacturing method

    Isna, Lathifa Rusita / Nugroho, Afid / Pratomo, Rezky Agung et al. | American Institute of Physics | 2023


    Mechanical Properties and Optimization Analysis on Battery Box with Honeycomb Sandwich Composite Structure

    Zhao, Ying / Shi, Jinyu / Wang, Kaifeng et al. | Springer Verlag | 2023


    Aluminum honeycomb sandwich composite board

    CHEN JUN / XU DONGGUANG / YAO LIJUN et al. | Europäisches Patentamt | 2024

    Freier Zugriff

    ARGOMENTI VARI

    Online Contents | 1997