A new dual-layer carbon phenolic manufactured from a three-dimensional woven substrate was tested in three arcjet facilities over a range of environments up to heat flux of approximately 6    kW / cm 2 at pressure of 5 bar. Sample geometries included both stagnation and wedge models. Based on property measurements and the observed material response, a midfidelity thermal response and ablation model was developed. The material and tests are described, and predictions of recession and temperature are compared with the arcjet test data.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Arcjet Tests and Thermal Response Analysis for Dual-Layer Woven Carbon Phenolic


    Beteiligte:
    Milos, Frank S. (Autor:in) / Chen, Yih-Kanq (Autor:in) / Mahzari, Milad (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    01.05.2018




    Medientyp :

    Aufsatz (Konferenz) , Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch




    Arcjet Tests and Thermal Response Analysis for Dual-Layer Woven Carbon Phenolic

    Milos, Frank S. / Chen, Yih-Kanq / Mahzari, Milad | AIAA | 2017


    Arcjet Tests and Thermal Response Analysis for Dual-Layer Woven Carbon Phenolic (AIAA 2017-3353)

    Milos, Frank S. / Chen, Yih-Kanq / Mahzari, Milad | British Library Conference Proceedings | 2017


    Conformal Phenolic Impregnated Carbon Ablator Arcjet Testing, Ablation, and Thermal Response

    Milos, Frank S. / Gasch, Matthew J. / Prabhu, Dinesh K. | AIAA | 2015