A novel class of ablative materials using phenolic resin, silica fabric, and nano-zirconium dioxide is being developed as a potential alternative for use in high-heat-flux thermal protection applications. Four new silica–phenolic ablatives have been fabricated using tandem nanocomposite formulations. Each of the tandem composites consist of nano-zirconium dioxide with small amounts of one of the following additives: multiwalled carbon nanotubes, nano-graphene platelets, alumina nanofibers, and nano-boron carbide. Materials have been fabricated, characterized, and compared using thermal and microanalysis. Thermogravimetric analysis and microscale combustion calorimetry were used to compare char yield, thermal stability, and flammability properties. Oxy-acetylene test bed aerothermal ablation testing was used to evaluate the composites under a high heat flux of 1000    W / cm 2 environment. Data analysis on recession rate, mass loss rate, backside heat-soaked temperature, surface temperature, and materials surface behavior were collected and used as a comparison tool to rank ablation performance of candidate materials. After testing of the candidates, it was determined that the nanocomposite containing nano-boron carbide in tandem with nano-zirconium dioxide was the best-performing candidate, demonstrating superior ablation properties, such as mass loss, recession rate, and insulative properties.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Silica–Phenolic Nanocomposite Ablatives for Thermal Protection Application


    Beteiligte:
    Fahy, William P. (Autor:in) / Langston, Jon (Autor:in) / Wu, Hao (Autor:in) / Koo, Joseph H. (Autor:in) / Kim, Steven (Autor:in) / Misasi, Dana (Autor:in) / Parra, Ruby (Autor:in) / Canan, Luke (Autor:in) / Li, Kara (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    2020-04-14


    Format / Umfang :

    7 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Nozzle designs with pitch precursor ablatives

    BLEVINS, H. / BEDARD, R. | AIAA | 1976


    Determining Failure Time for Weak-Char Ablatives

    Bruns, Morgan / Ezekoye, Ofodike / Koo, Joseph | AIAA | 2007


    BIOBASIERTES ABLATIVES THERMALSCHUTZMATERIAL MIT MECHANISCHER FUNKTION

    GÜNTHER RAPHAELA ELISA / UNBEHAUN HOLGER | Europäisches Patentamt | 2024

    Freier Zugriff

    Determining Failure Time for Weak-Char Ablatives AIAA Paper

    Bruns, M. / Ezekoye, O. / Koo, J. et al. | British Library Conference Proceedings | 2007