A 60 wt% boron nitride (BN)–40 wt% silica ( SiO 2 ) hot-pressed composite, denoted as M26, was used as the insulating chamber wall for a xenon plasma Hall-effect thruster operated for approximately 2000 h at power levels between 1.5 and 5 kW. The chamber wall showed a range of erosion microstructures. In the heavily eroded regions, striations in the surface topology were evident with surface protrusions in the generic shape of conical tips consisting of stratified BN and silica phases. Microcracking along the long axis of the BN basal plane was prevalent. Through a two-dimensional finite element model, the microcracking has been determined to occur because of the anisotropic thermal expansion of BN in the amorphous silica matrix. Exfoliation accompanied the microcracking in BN and resulted in the preferential loss of BN as compared with silica in these heavily eroded regions.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Plasma-Induced Erosion on Ceramic Wall Structures in Hall-Effect Thrusters


    Beteiligte:

    Erschienen in:

    Erscheinungsdatum :

    01.05.2014




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Metallic wall hall thrusters

    GOEBEL DAN MICHAEL / HOFER RICHARD ROBERT / MIKELLIDES IOANNIS G | Europäisches Patentamt | 2018

    Freier Zugriff

    METALLIC WALL HALL THRUSTERS

    GOEBEL DAN MICHAEL / HOFER RICHARD ROBERT / MIKELLIDES IOANNIS G | Europäisches Patentamt | 2016

    Freier Zugriff

    Metallic wall hall thrusters

    GOEBEL DAN MICHAEL / HOFER RICHARD ROBERT / MIKELLIDES IOANNIS G | Europäisches Patentamt | 2016

    Freier Zugriff

    Conducting Wall Hall Thrusters

    Goebel, Dan M. / Hofer, Richard R. / Mikellides, Ioannis G. et al. | AIAA | 2013