In this work, the effects of cellulose nanofibrils (CNFs) on workability, hydration reaction, microstructure, early age shrinkage, fracture properties, flexural strength, and compressive strength of cement paste were investigated. Six batches with variable CNF concentrations with the same water-to-cement (w/c) ratio (0.35) were tested. Flow table test showed a reduction in the workability as CNF dosage increased. Isothermal calorimetry (IC) tests showed that after 3 days, degree of hydration (DOH) improved up to 8% because of the addition of CNFs. Thermogravimetric analysis (TGA) tests at 7 and 28 days showed no significant changes in DOH for all pastes. After 7 days, mixture with 0.15% CNF resulted in up to 31% improvement in compressive strength. For 0.09% CNF addition, cement paste showed 26% increase in compressive strength after 28 days. Tests revealed that adding a small quantity of CNF (0.06%) along with entraining 0.05 extra water reduces autogenous shrinkage by 49% at a cement paste with w/c = 0.30. For interpreting the results, a tunnels, reservoirs, and bridges (TR&B) model is proposed. This model suggests that, as proposed by others, CNFs can modify microstructure by providing tunnels for transporting water to unhydrated cement grain. Because of their hydrophilicity, CNFs retain water and work as reservoirs (internal curing), which explains the improvement in properties at low w/c ratios. Significant increases in fracture energy (up to 60%) and flexural strength (up to 116%) suggest that CNFs are an effective toughening mechanism, acting as bridges that increase the energy required for crack propagation.


    Zugriff

    Download

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Hydration and Early Age Properties of Cement Pastes Modified with Cellulose Nanofibrils


    Weitere Titelangaben:

    Transportation Research Record


    Beteiligte:


    Erscheinungsdatum :

    2020-08-08




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Hydration of ultrafine and ordinary Portland cement at early ages

    Chen, Xudong / Zhou, Jikai / Yan, Yuanyuan | Springer Verlag | 2014



    Hydration of ultrafine and ordinary Portland cement at early ages

    Chen, Xudong / Zhou, Jikai / Yan, Yuanyuan | Online Contents | 2014