The effectiveness of a vapor-deposited Cu-Cr coating in protecting a NARloy-Z (Cu-3 wt.%Ag-0.5 wt.%Zr) substrate was investigated in a hydrogen/oxygen rocket engine test facility. The rocket facility generated high-temperature, high-pressure flows of combustion gas. The Cu-Cr-coated NARloy-Z article was actively cooled by cryogenic gaseous hydrogen so that the coating surface temperature was maintained below 650 degree C. The coating provided good protection for the NARloy-Z substrate under both hydrogen- and oxygen-rich hot gas environments. In erosion tests (hydrogen rich), the coating remained as a metallic mixture of Cu and Cr phases. In the erosion/oxidation tests (oxygen rich), the coating surface formed a protective Cr2O3 scale under a thin layer of Cu-oxides. The ability of the coating to withstand repetitive thermal shocks from the hot gas impingement without cracking was attributed to the close match of thermal expansion properties between the Cu-Cr coating and the NARloy-Z substrate.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Hot gas erosion resistance of a vapor-deposited Cu-Cr coating


    Beteiligte:
    Chiang, K.T. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1999


    Format / Umfang :

    6 Seiten, 13 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Plasma vapor deposited (PVD) coating process

    HAACK LARRY P / STRACCIA ANN MARIE / SIMKO STEVEN J | Europäisches Patentamt | 2019

    Freier Zugriff



    Articles, including wheels, having plasma vapor deposited (PVD) coating

    HAACK LARRY P / STRACCIA ANN MARIE / SIMKO STEVEN J | Europäisches Patentamt | 2016

    Freier Zugriff