The AerMet 310 alloy is a companion to the high-strength AerMet 100 alloy. Both are nickel-cobalt alloys having very good ductility. The ultimate tensile strength (UTS) of AerMet 310 is 2172 MPa which is higher than the maximum 2082 MPa UTS reached by the AerMet 100 when aged at 468 degree C and the typical UTS of 1965 MPa when aged at 482 degree C. The AerMet 310 and 100 alloys have similar composite ratio averages, both greater than those of the Marage 300, 250, and 300 M alloys, indicating that the AerMet alloys have stress corrosion cracking resistance that is significantly better than that of the other three high-strength alloys.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Airframe and landing gear alloy


    Beteiligte:
    Dahl, J.M. (Autor:in) / Novotny, P.M. (Autor:in)

    Erschienen in:

    Erscheinungsdatum :

    1999


    Format / Umfang :

    3 Seiten



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Reduction of Airframe Noise from Landing Gear

    Choi Chow, Leung | Online Contents | 2000


    Research into Landing Gear Airframe Noise Reduction

    Dobrzynski, Werner / Chow, Leung / Guion, Pierre et al. | AIAA | 2002


    Landing Gear Door Liners for Airframe Noise Reduction

    Jones, Michael G. / Howerton, Brian M. / Van De Ven, Thomas | NTRS | 2014


    A European study on landing gear airframe noise sources

    Dobrzynski, W. / Chow, L. / Guion, P. et al. | AIAA | 2000


    Application of Composites to Helicopter Airframe and Landing Gear Structures

    M. J. Rich / G. F. Ridgley / D. W. Lowry | NTIS | 1973