A new class of large, high-speed seagoing ferry-boat is under development for service around the world. The ships, which are built entirely of aluminum-alloy plate and stiffeners, show a propensity for fatigue cracking of the welded structure. Cracks may occur in both the hulls and the superstructure early in their 20-year service life. Early appearance of fatigue cracks is shown to result from the combined stress and strain fields set up in weld zones by the static residual stresses and cyclic loads, beyond the effects of weld and detail geometry. A numerical example demonstrates that conventional methods of fatigue analysis overestimate the lifetime of the welded aluminum structure, while damage tolerance analysis based on fracture mechanics leads to improved prediction.


    Zugriff

    Zugriff über TIB

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Considerations of the effect of residual stresses on fatigue of welded aluminum alloy structures


    Beteiligte:
    Berkovits, A. (Autor:in) / Kelly, D.W. (Autor:in) / Di, S. (Autor:in)


    Erscheinungsdatum :

    1998


    Format / Umfang :

    12 Seiten, 24 Quellen




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Print


    Sprache :

    Englisch




    Residual stresses in welded structures

    Leggatt, R.H. | Tema Archiv | 2008


    Residual stresses in welded structures

    Rossell, H.E. | Engineering Index Backfile | 1942



    Fatigue Endurance of Welded Joints, Residual Stresses and Fatigue Improvement Treatments

    Trufyakov / Mikheev / Kudryavsten et al. | British Library Conference Proceedings | 1993


    Residual stresses in welded ships

    Pierce, H.W. | Engineering Index Backfile | 1942